The properties of nanometric-sized helium bubbles in silicon have been investigated using both spatially resolved electron-energy-loss spectroscopy combined with a recently developed method, and molecular-dynamics simulations. The experiments allowed for an accurate determination of size, aspect ratio, and helium density for a large number of single bubbles, whose diameters ranged from 6 to 20 nm. Very high helium densities, from 60 to 180 He nm−3, have been measured depending on the conditions, in stark contrast with previous investigations of helium bubbles in metal with similar sizes. To supplement experiments on a smaller scale, and to obtain insights into the silicon matrix state, atomistic calculations have been performed for helium bubbles in the diameter range 1–13 nm. Molecular-dynamics simulations revealed that the maximum attainable helium density is critically related to the strength of the silicon matrix, which tends to yield by amorphization at the highest density levels. Calculations give helium density values for isolated single bubbles that are typically lower than measurements. However, excellent agreement is recovered when the interactions between bubbles and the presence of helium interstitials in the matrix are taken into account. Both experiments and numerical simulations suggest that the Laplace-Young law cannot be used to predict helium density in nanometric-sized bubbles in a covalent material such as silicon.
-
Archives
- October 2023
- September 2023
- August 2023
- February 2023
- January 2023
- June 2022
- January 2022
- September 2021
- August 2021
- July 2021
- June 2021
- May 2021
- March 2021
- February 2021
- January 2021
- December 2020
- October 2020
- September 2020
- August 2020
- July 2020
- June 2020
- May 2020
- April 2020
- March 2020
- February 2020
- January 2020
- December 2019
- November 2019
- October 2019
- September 2019
- August 2019
- July 2019
- June 2019
- May 2019
- April 2019
- March 2019
- February 2019
- January 2019
- December 2018
- November 2018
- October 2018
- September 2018
- August 2018
- July 2018
- June 2018
- May 2018
- April 2018
- March 2018
- February 2018
- January 2018
- November 2017
- October 2017
- September 2017
- August 2017
- July 2017
- June 2017
- May 2017
- April 2017
- March 2017
- February 2017
- December 2016
- November 2016
- October 2016
- September 2016
- August 2016
- July 2016
- June 2016
- May 2016
- April 2016
- January 2016
- December 2015
- November 2015
- October 2015
- September 2015
- August 2015
- July 2015
- June 2015
- May 2015
- April 2015
- March 2015
- February 2015
- January 2015
- December 2014
- November 2014
- October 2014
- September 2014
- August 2014
- July 2014
- June 2014
- May 2014
- April 2014
- March 2014
- February 2014
- January 2014
- December 2013
- November 2013
- October 2013
- September 2013
- August 2013
- July 2013
- May 2013
- April 2013
- February 2013
- January 2013
- December 2012
- November 2012
-
Meta